Comparing Fracture Resistance of Monolithic Zirconia Crowns Designed with three Different Thicknesses: An In Vitro Study

Safa M. Alzoubi; Abdel Ghani Alsahhar; Ebtisam Alsalameh

doi:10.33891/FSZ.114.4.172-177

Safa M. Alzoubi Department of Fixed Prosthodontics,Faculty of Dentistry, University of Hama, Syria https://orcid.org/0000-0002-5275-7967
Abdel Ghani Alsahhar Faculty of Public Health, University of Debrecen, Hungary https://orcid.org/0000-0002-8062-8791
Ebtisam Alsalameh Department of Fixed Prosthodontics,Faculty of Dentistry, University of Hama, Syria https://orcid.org/0000-0002-1283-2002

DOI: https://doi.org/10.33891/FSZ.114.4.172-177

Kulcsszavak: törés, ellenállás, monolit, cirkónium, koronák, vastagság

Absztrakt

A beszűkült interokkluzális tér mindig komoly kihívást jelent a gyakorló fogorvosok számára, hogy esztétikailag kifogástalan
restaurátumokat készítsenek, és ugyanakkor a lehető legnagyobb keményállományt is megőrizzék a fogakból.
Jelen vizsgálat célja a második generációs CAD/CAM technikával készült monolitikus cirkónium-dioxid restaurátumok
vastagsága és törési ellenállása közötti kapcsolat vizsgálata és annak meghatározása, hogy milyen mértékben lehet
a korona vastagságát csökkenteni, elsősorban a moláris régióban, ott, ahol az interokkluzális tér csekély és a rágóerő a
legnagyobb.
30 különböző tervezésű monolitikus cirkónium-dioxid koronát készítettek a második generációs CAD-CAM technológiával,
amelyeket az okkluzális vastagság alapján három egyenlő számú [10] csoportra osztottak: A csoport 2 mm;
B csoport 1,5 mm és C csoport 1 mm.
A tesztkoronákat előkészített, extrahált természetes fogakra (felső premolárisok) rögzítették üvegionomér cementtel,
majd ezeket a koronákat mechanikai vizsgálatnak vetették alá. Megállapították, hogy a monolitikus cirkónium-dioxid koronák
törésállóságát jelentősen befolyásolta a vastagságuk. A vastagság növekedésével a törési ellenállás folyamatosan
javult. Arra a következtetésre jutottak, hogy még az 1 mm vastag monolitikus cirkónium-dioxid restaurátum is elég erős
volt ahhoz, hogy a moláris régióban ellenálljon a fiziológiás körülmények között fellépő maximális okkluzális megterhelésnek.
Következésképen a moláris régióban a monolitikus cirkónium-dioxid restaurátumok vastagsága megbízhatóan
1 mm-re csökkenthető.

Hivatkozások

Kern F, Reveron H, Chevalier J, Gadow R. Mechanical behaviour of extremely tough TZP bioceramics. J Mech Behav Biomed Mater. 2019 Feb;90:395-403. https://doi.org/10.1016/j.jmbbm.2018.11.001

Shahmiri R, Standard OC, Hart JN, Sorrell CC. Optical properties of zirconia ceramics for esthetic dental restorations: A systematic review. J Prosthet Dent. 2018 Jan;119(1):36-46. https://doi.org/10.1016/j.prosdent.2017.07.009

Kisi EH, Howard CJ. Crystal Structures of Zirconia Phases and their Inter-Relation. Key Eng Mater. 1998 Feb;153-154:1-36. https://doi.org/10.4028/www.scientific.net/KEM.153-154.1

Güth J-F, Stawarczyk B, Edelhoff D, Liebermann A. Zirconia and its novel compositions: What do clinicians need to know? Quintessence Int Berl Ger 1985. 2019;50(7):512-20. https://doi.org/10.3290/j.qi.a42653

Zhang Y, Lawn BR. Novel Zirconia Materials in Dentistry. J Dent Res. 2018 Feb;97(2):140-7. https://doi.org/10.1177/0022034517737483

Zhang F, Inokoshi M, Batuk M, Hadermann J, Naert I, Van Meerbeek B, et al. Strength, toughness and aging stability of highly-translucent Y-TZP ceramics for dental restorations. Dent Mater Off Publ Acad Dent Mater. 2016 Dec;32(12):e327-37. https://doi.org/10.1016/j.dental.2016.09.025

Stawarczyk B, Keul C, Eichberger M, Figge D, Edelhoff D, Lümkemann N. Three generations of zirconia: From veneered to monolithic. Part II. Quintessence Int Berl Ger 1985. 2017;48(6):441-50. https://doi.org/10.3290/j.qi.a38157

Stawarczyk B, Ozcan M, Hallmann L, Ender A, Mehl A, Hämmerlet CHF. The effect of zirconia sintering temperature on flexural strength, grain size, and contrast ratio. Clin Oral Investig. 2013 Jan;17(1):269-74. https://doi.org/10.1007/s00784-012-0692-6

Jasim HH, Findakly MB, Mahdi NA, Mutar MT. Effect of Reduced Occlusal Thickness with Two Margin Designs on Fracture Resistance of Monolithic Zirconia Crowns. Eur J Dent. 2020 Mar;14(2):245-9. https://doi.org/10.1055/s-0040-1709342

Nordahl N, Vult von Steyern P, Larsson C. Fracture strength of ceramic monolithic crown systems of different thickness. J Oral Sci. 2015 Sep;57(3):255-61. https://doi.org/10.2334/josnusd.57.255

Elsayed A, Meyer G, Wille S, Kern M. Influence of the yttrium content on the fracture strength of monolithic zirconia crowns after artificial aging. Quintessence Int Berl Ger 1985. 2019;50(5):344-8. https://doi.org/10.3290/j.qi.a42097

Tang YL, Kim J-H, Shim J-S, Kim S. The effect of different cooling rates and coping thicknesses on the failure load of zirconia-ceramic crowns after fatigue loading. J Adv Prosthodont. 2017 Jun;9(3):152-8. https://doi.org/10.4047/jap.2017.9.3.152

Kontonasaki E, Rigos AE, Ilia C, Istantsos T. Monolithic Zirconia: An Update to Current Knowledge. Optical Properties, Wear, and Clinical Performance. Dent J. 2019 Sep 2;7(3):E90. https://doi.org/10.3390/dj7030090

Alraheam IA, Donovan T, Boushell L, Cook R, Ritter AV, Sulaiman TA. Fracture load of two thicknesses of different zirconia types after fatiguing and thermocycling. J Prosthet Dent. 2020 Apr;123(4):635-40. https://doi.org/10.1016/j.prosdent.2019.05.012

Hidaka O, Iwasaki M, Saito M, Morimoto T. Influence of clenching intensity on bite force balance, occlusal contact area, and average bite pressure. J Dent Res. 1999 Jul;78(7):1336-44. https://doi.org/10.1177/00220345990780070801

Sun T, Zhou S, Lai R, Liu R, Ma S, Zhou Z, et al. Load-bearing capacity and the recommended thickness of dental monolithic zirconia single crowns. J Mech Behav Biomed Mater. 2014 Jul;35:93-101. https://doi.org/10.1016/j.jmbbm.2014.03.014

Sorrentino R, Triulzio C, Tricarico MG, Bonadeo G, Gherlone EF, Ferrari M. In vitro analysis of the fracture resistance of CAD-CAM monolithic zirconia molar crowns with different occlusal thickness. J Mech Behav Biomed Mater. 2016 Aug;61:328-33. https://doi.org/10.1016/j.jmbbm.2016.04.014

Nakamura K, Ankyu S, Nilsson F, Kanno T, Niwano Y, Vult von Steyern P, et al. Critical considerations on load-to-failure test for monolithic zirconia molar crowns. J Mech Behav Biomed Mater. 2018 Nov;87:180-9. https://doi.org/10.1016/j.jmbbm.2018.07.034

Zimmermann M, Ender A, Mehl A. Influence of CAD/CAM Fabrication and Sintering Procedures on the Fracture Load of Full-Contour Monolithic Zirconia Crowns as a Function of Material Thickness. Oper Dent. 2020 Apr;45(2):219-26. https://doi.org/10.2341/19-086-L

Hamza TA, Sherif RM. Fracture Resistance of Monolithic Glass-Ceramics Versus Bilayered Zirconia-Based Restorations. J Prosthodont Off J Am Coll Prosthodont. 2019 Jan;28(1):e259-64. https://doi.org/10.1111/jopr.12684

Burke FJ. Maximising the fracture resistance of dentine-bonded all-ceramic crowns. J Dent. 1999 Mar;27(3):169-73. https://doi.org/10.1016/S0300-5712(98)00050-5

Három különböző vastagságú monolit cirkónium korona törési ellenállásnak in vitro összehasonlító vizsgálata